适合冷冻修边工艺的条件：

Material Suitable for Cryogenic Deflashing Machine 

Rubber                        NR NBR HNBR CR EPDM FKM ACM SILICONE

Precision Plastic        PA+GF PC+GF PPS POM PUR PBT TPU TPE TPR     

Die-casting Alloy       ZINC ALLOY   MAG ALLOY
Small and Round shape will be more suitable for the cryogenic deflashing.
      Some Component Material Examples

Flash Condition Suitable for Cryogenic Deflashing Machine
To consistently get a quality-finished-part, you have to consistently put in a quality unfinished-part. 
Flash: Make the flash of your moulded product as thin as possible (<0.2mm), with as good a flash base as possible, or, in the case where sealing surfaces are involved, try to move the flash away from the critical areas.
Overflows should, if they are necessary for your molding process, be moved to a suitable distance away from the part as possible.
Tear trim design was developed to eliminate the cryogenic deflashing operation. The overflow is placed extremely close to the part so that, when this overflow is removed by hand, no flash remains. (If there’s tear trim…Keep atleast 0.3mm from parts)
Parting Lines: Your moulded parts need a clear, consistent demarcation of flash. For best results, the parting line should not exceed 0.127 mm thickness.
It is important to understand that no cryogenic deflashing unit will eliminate your molding problems. 
Also check following Mould Design Technical Drawing for you better understand how to be most suitable for cryogenic Deflashing Technology.